#BR400/590TR,BR400/590TR steel,BR400/590TR steel plate,BR400/590TR steel sheet supplier,BR400/590TR steel price

TRIP Steel is the abbreviation of Transformation Induced Plastics steel. As one of AHSS, the microstructure of TRIP steel is made up of ferrite, bainite and retained austenite. It has solved the contradiction between strength and ductility. It has high strength while it has good plasticity, too. This specific property can meet the formation requirements of automobile parts with complex shape which the good ducticity is needed.

BR400/590TR steel mechanical properties
Grade
Thickness
(mm)
Yield strength
(MPa)
Tensile strength
(MPa)
Elongation
A50
(%)
BR400/590TR
1.6~6.0
≥400
≥590
≥24
BR400/590TR steel Chemical Composition
Grade
C
Si
Mn
Nb + Ti
BR400/590TR
＜0.3
＜2.2
＜2.5
0~0.10

The strength and formability of BR400/590TR is much more excellent than normal high strength steel ,Thanks to the combination of high strength and good formability ,the BR450/780TR is a preferred material for automobile industry.
HENAN JOIN-WIN IM/EX CORP Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As BR400/590TR Mechanical and BR400/590TR suppliers, we can supply BR400/590TR Chemical, BR400/590TR Mechanical and BR400/590TR standard for you ,please contact us :

Email : pandora@steel-jw.com
Skype : pandora.peng

评论

发表评论

此博客中的热门博文

#Automotive B750L steel,B750L steel plate,B750L steel sheet,B750L steel supplier,B750L steel price,B750L steel plate manufacturer

图片
B750L automotive high-strength steel using advanced smelting technology, low inclusion content, pure steel, has good formability and high fatigue properties, it can be used in the manufacture of complex shapes B750L steel Chemical composition % Grade C Si Mn p S Al Nb V Ti Mo B750L ≤0.10 ≤0..50 ≤2.10 ≤0.025 ≤0.010 ≥0.015 ≤0.09 ≤0.20 ≤0.15 ≤0.50 B750L steel Mechanical Properties Grade Yield strength (MPa) Tensile strength (MPa) Elongation (%) 180 degree cold bend, diameter Thickness＜3mm Lo=80mm, b=20mm Thickness≥3mm L0=5.65√S0 B750L ≥750 800-950 ≥10 ≥12 2.0a B750L steel CE Grade CE C,% CE Carbon equivalent (CE) B750L ≤0.08 0.40 CE = C + Mn/6
阅读全文

#Automotive QSTE380TM,QSTE380TM steel,QSTE380TM steel plate,QSTE380TM steel sheet manufacturer,QSTE380TM steel plate supplier

图片
QStE380TM steel is fine-grained steel with good cold formability. For applications requiring good cold formability and have a higher or high strength requirements of automobile frames, beams and other automotive structural parts. QStE380TM steel sheet Chemical analysis -% by mass* Grade C Si Mn P S 1) Altotal Mo Ti V max. max. max. max. max. min. max. max. max. QStE380TM 0,12 0,50 1,40 0,03 0,025 0,015 - 0.15 0.20 QStE380TM steel plate Mechanical properties Mechanical properties Yield Strength ReH [N/mm2] transv.min. Tensile Strength Rm [N/mm2] transv. Min.totalelongation [%] Smallest recommended bending radius bending angles ≤ 90 QStE380 TM 380 450 - 590 L0 = 80 mm e
阅读全文

#B320L steel,B320L steel plate,B320L steel sheet,Automotive B320L steel plate,#Automotive B320L steel sheet manufacturer

图片
B320L belong to cold-rolled sheet, cold-rolled sheet is hot rolled coils as raw material at room temperature at a temperature below the recrystallization rolling from, including board and volumes. B320L steel plate, steel strip is a kind of Hot-rolled pickled steel for automotive wheel is low carbon micro-alloyed steel with excellent properties of cold forming and welding produced by using advanced TMCP technology. B320L steel mechanical property Grade Tensile test Yield strength Tensile strength Yield ratio Elongation after fracture A L0=5.65√S0 (%) 180°Bending Test b Diameter B320L ≥215 320-420 -- ≥27 0a B320L steel chemical composition Grade Chemical composition(Heat analysis)% C Si Mn P S Alt B320L ≤0.10 ≤0.30 ≤0.05 ≤0.030 ≤0.025
阅读全文