#B700QZR steel,B700QZR steel plate,B700QZR steel sheet,B700QZR steel supplier,B700QZR steel plate price,B700QZR steel plate manufacturer

Wheel is made up of the rim and the disk. The main processing technique for rim is roll forming. Punch forming and spin forming are usually applied for disc. Punch forming is mainly used for disc of passenger cars, while disc of commercial cars are usually punch-formed (wigh inner tire) or spin-formed (without inner tire)

B700QZR steel mechanical properties
Grade
Yield strength
(MPa)
Tensile strength
(MPa)
Elongation
(%)
180 degree cold bend,diameter
B700QZR
≥600
700~850
≥13
1.5a

Remark : Test piece for tensile test taken to the rolling direction. Test piece for cold bend test taken transverse to the rolling direction.

HENAN JOIN-WIN IM/EX CORP Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B700QZR Mechanical and B700QZR suppliers, we can supply B700QZR Chemical, B700QZR Mechanical and B700QZR standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

评论

发表评论

此博客中的热门博文

#Automotive B750L steel,B750L steel plate,B750L steel sheet,B750L steel supplier,B750L steel price,B750L steel plate manufacturer

图片
B750L automotive high-strength steel using advanced smelting technology, low inclusion content, pure steel, has good formability and high fatigue properties, it can be used in the manufacture of complex shapes B750L steel Chemical composition % Grade C Si Mn p S Al Nb V Ti Mo B750L ≤0.10 ≤0..50 ≤2.10 ≤0.025 ≤0.010 ≥0.015 ≤0.09 ≤0.20 ≤0.15 ≤0.50 B750L steel Mechanical Properties Grade Yield strength (MPa) Tensile strength (MPa) Elongation (%) 180 degree cold bend, diameter Thickness＜3mm Lo=80mm, b=20mm Thickness≥3mm L0=5.65√S0 B750L ≥750 800-950 ≥10 ≥12 2.0a B750L steel CE Grade CE C,% CE Carbon equivalent (CE) B750L ≤0.08 0.40 CE = C + Mn/6
阅读全文

#Automotive QSTE380TM,QSTE380TM steel,QSTE380TM steel plate,QSTE380TM steel sheet manufacturer,QSTE380TM steel plate supplier

图片
QStE380TM steel is fine-grained steel with good cold formability. For applications requiring good cold formability and have a higher or high strength requirements of automobile frames, beams and other automotive structural parts. QStE380TM steel sheet Chemical analysis -% by mass* Grade C Si Mn P S 1) Altotal Mo Ti V max. max. max. max. max. min. max. max. max. QStE380TM 0,12 0,50 1,40 0,03 0,025 0,015 - 0.15 0.20 QStE380TM steel plate Mechanical properties Mechanical properties Yield Strength ReH [N/mm2] transv.min. Tensile Strength Rm [N/mm2] transv. Min.totalelongation [%] Smallest recommended bending radius bending angles ≤ 90 QStE380 TM 380 450 - 590 L0 = 80 mm e
阅读全文

#B320L steel,B320L steel plate,B320L steel sheet,Automotive B320L steel plate,#Automotive B320L steel sheet manufacturer

图片
B320L belong to cold-rolled sheet, cold-rolled sheet is hot rolled coils as raw material at room temperature at a temperature below the recrystallization rolling from, including board and volumes. B320L steel plate, steel strip is a kind of Hot-rolled pickled steel for automotive wheel is low carbon micro-alloyed steel with excellent properties of cold forming and welding produced by using advanced TMCP technology. B320L steel mechanical property Grade Tensile test Yield strength Tensile strength Yield ratio Elongation after fracture A L0=5.65√S0 (%) 180°Bending Test b Diameter B320L ≥215 320-420 -- ≥27 0a B320L steel chemical composition Grade Chemical composition(Heat analysis)% C Si Mn P S Alt B320L ≤0.10 ≤0.30 ≤0.05 ≤0.030 ≤0.025
阅读全文