Sales #B500CL steel,B500CL steel plate,B500CL steel supplier,B500CL steel #sheet price,B500CL steel sheet manufacturer,B500CL steel plate

B500CL steel has high strength, good fatigue resistance, plasticity and good weldability

B500CL steel Chemical Composition %
Grade
C
Si
Mn
Nb + Ti
P
S
B500CL
≤0.10
≤0.50
≤1.5
≤0.10
≤0.025
≤0.010

B500CL steel Mechanical Properties
Grade
Thickness(mm)
Yield strength
(MPa)
Tensile strength
(MPa)
Elongation A50 (%)
B500CL
1.8~12.0
≥400
500~650
≥26

B500CL steel Processing
Wheel is made up of the rim and the disk. The main processing technique for rim is roll forming. Punch forming and spin forming are usually applied for disc. Punch forming is mainly used for disc of passenger cars, while disc of commercial cars are usually punch-formed (wigh inner tire) or spin-formed (without inner tire).

HENAN JOIN-WIN IM/EX CORP will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B500CL Mechanical and B500CL suppliers, we can supply B500CL Chemical, B500CL Mechanical and B500CL standard for you ,please contact us :

Email : pandora@steel-jw.com
Skype : pandora.peng

评论

发表评论

此博客中的热门博文

Sales BR290/440HE,BR290/440HE steel plate,BR290/440HE steel supplier,BR290/440HE steel price

图片
BR290/440HE has high strength, good elongation, food formability and flangeability, which can meet the forming requirement of auto parts with complex shapes, such as lower arm, etc. It can also be applied to other parts that need flanging. The flangeability is expressed by the hole expansion ratio. Hole expansion ratio is one of criteria to the formability of steels. It reflects the material’s resistance to local cracking because of large local stretch in the direction perpendicular to the hole during hole expansion. BR290/440HE steel mechanical properties Grade Thickness (mm) Tensile strength (MPa) Yield strength (MPa) Elongation A50 (%) Hole expansion rate (%) BR290/440HE 1.6~6.0 ≥440 ≥290 ≥28 ≥100 BR290/440HE steel Chemical composition % Grade C Si Mn Nb + Ti BR290/440HE ＜0.10 ＜1.50 0.5~2.0 0~...
阅读全文

Sales BR340/490HE steel,BR340/490HE steel plate,BR340/490HE steel supplier,BR340/490HE steel sheet price

图片
 BR340/490HE has high strength, good elongation, food formability and flangeability, which can meet the forming requirement of auto parts with complex shapes, such as lower arm, etc. It can also be applied to other parts that need flanging. The flangeability is expressed by the hole expansion ratio. Hole expansion ratio is one of criteria to the formability of steels. It reflects the material’s resistance to local cracking because of large local stretch in the direction perpendicular to the hole during hole expansion. BR340/490HE steel mechanical properties Grade Thickness (mm) Tensile strength (MPa) Yield strength (MPa) Elongation A50 (%) Hole expansion rate (%) BR340/490HE 1.6~6.0 ≥490 ≥340 ≥24 ≥80 BR340/490HE steel Chemical composition % Grade C Si Mn Nb + Ti BR340/490HE ＜0.10 ＜1.50 0.5~2.0 ...
阅读全文

#B330CL steel,B330CL steel plate,B330CL steel sheet,Automotive B330CL steel plate,#Automotive B330CL steel sheet manufacturer

图片
B330CL thickness allowable deviation should be consistent with Q / BQB 301 high precision (PT.B) provisions, B330CL good cold formability for automotive roll forming wheel and spoke network. JW STEEL is specialized in supplying steel plate in B330CL from stock or directly from the mill to customer destinations on a global footing. B330CL Chemical composition Grade The Element Max (%) B330CL C Si Mn P S ≤0.10 ≤0.30 ≤0.50 ≤0.030 ≤0.025 Alt Nb V Ti ≥0.010 B330CL steel Mechanical Properties Grade Tensile(Mpa) Yield (Min Mpa) Elonggation(min%) B330CL 330-430 ≥225 ≥33 B330CL application: B330CL are featured with high strength ,excellent forming and weldingperformence and high dimension accuracy and surface-turers to make automo...
阅读全文